ERNiFeMn-Cl which has 44 percent Nickel Alloy was developed for all position gas metal arc, | ||||||
| gas tungsten arc and high speed automatic gas metal arc welding of nodular, grey,spheroidal | ||||||
| graphite and malleable cast irons to themselc or to other materials inclduing stainls |
| steel, carbon steel,low alloy steel and varous nickel com prsive loading Arcos | ||||||
| 2216 work hardens making it ideal for bearing surfac and as a cushioning layer for |
| hardsurfacing applications. |
| CLASSIFICATIONS: | ||||||
| ERNiFeMn-Cl | ||||||
| AWS A5.15 | ||||||
| AE SFA 5.15 | ||||||
| UNS N02216 | ||||||
| APPLICATIONS: | ||||||
| ERNiFeMn-Cl has been digned for welding high strength cast irons that are used in critical | ||||||
| applications such as automotive exhaust systems, catalytic converters,and other areas that |
| demand high strength at relatively high temperatur combined with ease od fabrication. |
| DIAMETERS: | ||||||
| 0.035'', 0.045'', 0.63'', | ||||||
| 3/32'',1/8'', | ||||||
| 5/32'',3/16'' | ||||||
| TYPICAL | ||||||
| MECHANICAL PROPERTI: | ||||||
| Tensile Strength (psi) 85,000 | ||||||
| Yield Strength (psi) 65,000 | ||||||
| Percent Elongation 15 | ||||||
| TYPICAL | ||||||
| CHEMICAL COMPOSTITON: | ||||||
| C | Mn | Ni | Fe | |||
| 0.30 | 12.30 | 42.80 | Remain | |||
| Cr | Mo | Fe | Co | |||
| 21.50 | 13.50 | 3.10 | 1.80 | |||